| 王志刚,丁大成,任金莲,刘纯荣,吴胜举,兰涛,刘学辉,赵永骞,王长京.超声雾化法制取金属粉末方法研究[J].,1994,12(4):34-38 |
| 超声雾化法制取金属粉末方法研究 |
| Investigation on Ultrasonic Atomization Process for Manufacturing Metalic Powders |
| |
| 中文摘要: |
| 本文介绍了利用超声振动能量制取超细金属粉末的超声雾化方法，提出了超声制粉雾化室，等离子枪，阴极、阳极喷咀及换能器振动系统的最佳尺寸和工作参数，给出了实验结果及制得的粉末显微结构照片．实验结果表明，用本文所述方法制得的金属粉末组成为：－80目粉占84呢，－120目粉占63．7啪，而用PREP方法制得的粉末分别占19．5％和11．7％，由此看来，用本方法制取超细金属粉，在粒度组成方面优于PREP方法．文中还对粉末冷却速度做了估算，得到了粉末平均冷却速度大于1×105k/5 |
| 英文摘要: |
| The ultrasonic atomization process for manufacturing superfine metallic:powderswas investigated. The optimium sizes and process parameters of the atomizationchamber, plasmatron, cathode, anodic nozzle and ultrasonic transducer are described,and the microstrcture of the powders made with the present system is presented.Experimental results indicate that granu]ar composition of the resulting powdersconsisting of 84 percent of -8o mesh powders and 63.7 percent of -l2O meshpowders is much better than that of PREP with respectively 19.5 percent and ll.7percent. The average cooling rate of the powders during the manufacturing processis calculated to be over 1 X lO5k per second. |
| DOI：10.11684/j.issn.1000-310X.1994.04.008 |
| 中文关键词: 超声雾化 金属粉末 冷却速度 超声换能器 等离子枪 声学研究所 陕西师范大学 金属研究 法制 超声振动系统 |
| 英文关键词: |
| 基金项目: |
|
| 摘要点击次数: 2479 |
| 全文下载次数: 550 |
|